• EN 10028:3 P355NL1    EN 10028:3 P355NL2     EN 10028:3 P355NH
• EN 10028:3 P460NH     EN 10028:3 P460NL2     EN 10028:3 P275NH   
• We also carry stocks of plates certified to EN 10028:2 P265GH

Chemical Requirements - P460NL1 (cast analysis, % by mass, maximum permitted unless indicated otherwise)

C	Si	Mn	P	S	Altotal *	N	Cr
0.20	0.60	1.10-1.70	0.025	0.015	0.020 min	0.025	0.30
Cu **	Mo	Nb	Ni	Ti	V	Nb+Ti+V
0.70	0.10	0.05	0.80	0.03	0.20	0.22

Tensile Requirements - P460NL1

Product Thickness	Yield Strength MPa	Tensile Strength MPa	Elongation A%
up to 16 mm	460 min	570 to 730	17 min
16 to 40 mm	445 min	570 to 720	17 min
over 40 to 60 mm	430 min	570 to 720	17 min
over 60 to 100 mm	400 min	540 to 710	17 min

Impact energy values for the normalised condition a) transverse

-50 OC	-40 OC	-20 OC	0 OC	+20 OC
-	27 J min	35 J min	50 J min	60 J min

b) longitudinal

-50oC	-40oC	-20oC	0 OC	+20oC
30 J min	40 J min	50 J min	70 J min	80 J min

 

Yield Steel Plate EN 10028:3 P460NL2

The designation EN 10028:3 P460NL2 shows that this is steel for pressure purposes (P) with minimum yield strength of 460 MPa (460) which is impact tested in the transverse direction at -50 deg C (NL2).

As well as P460NL2 we are stockists of other EN 10028:3 plates manufactured and certified to:

• EN 10028:3 P355NL1    EN 10028:3 P355NL2     EN 10028:3 P355NH
• EN 10028:3 P460NH     EN 10028:3 P460NL1     EN 10028:3 P275NH   
• We also carry stocks of plates certified to EN 10028:2 P265GH

Chemical Requirements - P460NL2 (cast analysis, % by mass, maximum permitted unless indicated otherwise)

C	Si	Mn	P	S	Altotal *	N	Cr
0.20	0.60	1.10-1.70	0.020	0.010	0.020 min	0.025	0.30
Cu **	Mo	Nb	Ni	Ti	V	Nb+Ti+V
0.70	0.10	0.05	0.80	0.03	0.20	0.22

 
Tensile Requirements - P460NL2

Product Thickness	Yield Strength MPa	Tensile Strength MPa	Elongation A%
up to 16 mm	460 min	570 to 730	17 min
16 to 40 mm	445 min	570 to 720	17 min
over 40 to 60 mm	430 min	570 to 720	17 min
over 60 to 100 mm	400 min	540 to 710	17 min

Impact energy values for the normalised condition a) transverse

-50 OC	-40 OC	-20 OC	0 OC	+20 OC
27 J min	30 J min	40 J min	60 J min	70 J min

b) longitudinal 

-50oC	-40oC	-20oC	0 OC	+20oC
42 J min	45 J min	55 J min	75 J min	85 J min

 

Yield Steel Plate EN 10028:3 P460NH

The specification EN 10028:3 covers a range of weldable fine grain steels supplied in the normalised condition and intended for pressure purposes. EN 10028:3 P460NH is steel for pressure purposes (P) with minimum yield strength of 460 MPa (460) which has specified elevated temperature properties (NH).

As well as P460NH we are stockists of other EN 10028:3 plates manufactured and certified to:

• EN 10028:3 P355NL1    EN 10028:3 P355NL2     EN 10028:3 P355NH
• EN 10028:3 P460NL1    EN 10028:3 P460NL2     EN 10028:3 P275NH
• We also carry stocks of plates certified to EN 10028:2 P265GH

Chemical Requirements (cast analysis, % by mass, maximum permitted unless indicated otherwise) 
Tensile Requirements 

 

Yield Steel Plate EN 10025:3 S460N

The specification EN 10025:3 covers weldable structural steels manufactured with a fine grain structure and supplied in the normalised condition or in an equivalent condition obtained by normalised rolling. There are four grades (S275, S355, S420 and S460) which indicate each grade’s minimum yield strength (in MPa) for plates 16 mm thick and below. Each grade is further sub-divided based on the specified minimum value of impact energy at a particular temperature. N indicates temperatures not lower than -20 deg C and NL not lower than -50 deg C.

The designation EN 10025:3 S460N shows that this is steel for structural purposes (S) with minimum yield strength of 460 MPa (460) which is impact tested at -20 deg C (N).

As well as S460N we are stockists of plates to EN 10025:3 S460NL

Chemical Requirements - S460N (cast analysis, % by mass, maximum permitted unless indicated otherwise)

C	Si	Mn	P	S	Altotal *	N	Cr
0.20	0.60	1.00-1.70	0.030	0.025	0.020 min	0.025	0.30
Cu **	Mo	Nb	Ni	Ti	V	Nb+Ti+V	Mo+Cr
0.55	0.10	0.05	0.80	0.05	0.20	0.22	0.30

Tensile Requirements - S460N

Product Thickness	Yield Strength MPa	Tensile Strength MPa	Elongation
up to 16 mm	460 min	540 to 720	17 min
16 to 40 mm	440 min	540 to 720	17 min
over 40 to 63 mm	430 min	540 to 720	17 min
over 63 to 80 mm	410 min	540 to 720	17 min
over 80 to 100 mm	400 min	540 to 720	17 min
over 100 to 150 mm	380 min	530 to 710	17 min
over 150 to 200 mm	370 min	530 to 710	17 min

 

Yield Steel Plate EN 10025:3 S460NL

The designation EN 10025:3 S460NL shows that this is steel for structural purposes (S) with minimum yield strength at 16 mm thick and below of 460 MPa (460) and which has specified minimum impact energy values at temperatures not lower than -50 deg C (NL).

As well as S460NL we are stockists of plates to EN 10025:3 S460N   

C	Si	Mn	P	S	Altotal *	N	Cr
0.20	0.60	1.00-1.70	0.025	0.020	0.020 min	0.025	0.30
Cu **	Mo	Nb	Ni	Ti	V	Nb+Ti+V	Mo+Cr
0.55	0.10	0.05	0.80	0.05	0.20	0.22	0.30

Tensile Requirements - S460NL

Product Thickness	Yield Strength MPa	Tensile Strength MPa	Elongation
up to 16 mm	460 min	540 to 720	17 min
16 to 40 mm	440 min	540 to 720	17 min
over 40 to 63 mm	430 min	540 to 720	17 min
over 63 to 80 mm	410 min	540 to 720	17 min
over 80 to 100 mm	400 min	540 to 720	17 min
over 100 to 150 mm	380 min	530 to 710	17 min
over 150 to 200 mm	370 min	530 to 710	17 min

Impact energy values for the normalised condition a) longitudinal

-50 OC	-40 OC	-30oC	-20 OC	-10oC	0 OC	+20 OC
27 J min	31 J min	40 J min	47 J min	51 J min	55 J min	63 J min